  • Poliol e isocianato para suela de zapato con cuña de dama
  • Poliol e isocianato para suela de zapato con cuña de dama
  • Poliol e isocianato para suela de zapato con cuña de dama
  • Poliol e isocianato para suela de zapato con cuña de dama
  • Poliol e isocianato para suela de zapato con cuña de dama
  • Poliol e isocianato para suela de zapato con cuña de dama

Poliol e isocianato para suela de zapato con cuña de dama

Payment Type:
L/C,T/T,D/P
Incoterm:
FOB,CFR,CIF
Min. Order:
300 Kilogram
Delivery Time:
15 Days
Transportation:
Ocean
Share:
  • DDescripción
Overview
Product Attributes

ModeloXC-9080W/XC-6088W

MarcaQuímico Xuchuan

Supply Ability & Additional Informations

Paquete20 y 225 kg / tambor

productividad250000

transporteOcean

Lugar de origenChina

HS-Code39095000

Tipo de PagoL/C,T/T,D/P

IncotermFOB,CFR,CIF

Plazo de entrega15 días

Packaging & Delivery
Selling Units:
Kilogram
Package Type:
20 y 225 kg / tambor
Poliol e isocianato para suela de zapato con cuña de dama

Detalle del producto

Application shoe sole
Keywords water soluble polyurethane resin
A/B Materials Temperatures(℃) A/B Materials Temperatures(℃)
A+C/B Mix ratio (By weight) 100/100~102
Cream Time (s) 6~8
End of Rise Time (s) 30~40
Free Rise Foam Density(g/cm3) 0.21~0.26
Mold Temperature(℃) 45~55
Demold Time(min) Demold Time(min)
Molded Density (g/cm3) 0.35~0.60

Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line

Application: Outsole, slippers, wedge shoes

Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40)

Density (g·cm-3/40)

Package(kg)

/

/

/

A-9080W

Cream,White,liquid

1000~1300

1.01~1.02

18

/

/

/

B-6088

Yellowish transparent liquid or waxy

600~800

1.08~1.2

20

/

/

/

Materials preheat

A-9080W:  preheated at 50~60 for 6~8 hours.

B-6088:    preheated at 50~60 for 6~8 hours.

Typical processing parameters & Reaction parameter.

Items

A/B Materials Temperatures()

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature()

Demold Time(min)

Parameter

40~45/38~42

100/100~102

6~8

30~40

0.21~0.26

45~55

5~7

The adding content of C-2 should be 210g±10g/18kg.

The adding content of water should be 0~80g/18kg according to the reality.

The adding content of hardener should be 0~1200g/18kg according to the reality.

Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore A )

Tensile strength
(MPa)

Elongation
(%)

Tear Strength
(kN/m)

Williams abrasion
(cc/php)

/

Physical  properties

0.35~0.60

60~88

4~7

200~300

11~20

130~200

/

Demold time may be prolonged with the increase of sole thickness.

These physical data are acquired by testing a sample of 6mm thick.

Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.


PERFIL DE LA COMPAÑÍA

PROCESO DE PRODUCCIÓN
CERTIFICACIÓN
EMBALAJE Y ENVÍO
Preguntas más frecuentes

CONTÁCTENOS

PRODUCTOS POR GRUPO : Sistema de poliuretano para suela de zapato > Sistema de poliuretano para suela de zapato de señora

Contactar proveedor
  • *A:
    Mr. LIU
  • *Mensaje:
    Su mensaje debe ser de entre 20 a 8,000 caracteres.

Lista de productos relacionados

Inicio

Phone

Información de la Empresa

solicitar