Casting de resina de poliuretano para la plantilla de suela media del zapato
Obtener el último precioTipo de Pago: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Cantidad de pedido mínima: | 1000 Kilogram |
transporte: | Ocean |
Hafen: | Shanghai |
Tipo de Pago: | L/C,T/T,D/P |
Incoterm: | FOB,CFR,CIF |
Cantidad de pedido mínima: | 1000 Kilogram |
transporte: | Ocean |
Hafen: | Shanghai |
Modelo: A-2001/B-8580
Marca: Químico xuchuan
Lugar De Origen: porcelana
Tipos De: Resina sintética y plásticos
Application: Insole and low density mid-sole
Characteristic: Good handle, low density and good dimension stability, high elasticity
Appearance: Liquid
Brand: Xuchuan
Code: A-2001/B-8580
Unidades de venta | : | Kilogram |
Tipo de paquete | : | 20 y 225 kg/tambor |
Ejemplo de una imagen | : |
Isocianato de poliol para la mitad de la suela
Casting de resina de poliuretano para la plantilla de suela media del zapato
SOLO SOLO PU QUÍMICO
Application | shoes insole |
A/B Materials Temperatures (℃) | 40~45/38~42 |
A+C/B Mix ratio (By weight) | 100/74~76 |
Cream Time (s) | 7~9 |
End of Rise Time (s) | 50~60 |
Free Rise Foam Density(g/cm3) | 0.13~0.16 |
Mold Temperature (℃) | 45~55 |
Molded Density (g/cm3) | 0.30~0.40 |
Hardness (Shore C ) | 35~45 |
Tensile strength(MPa) | Tensile strength(MPa) |
Characteristic: Good handle, low density and good dimension stability, high elasticity |
|||||||
Application: Insole and low density mid-sole |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
||
A-2001 |
Liquid |
1000~1400 |
1.01~1.02 |
18 |
|||
B-8580 |
Yellowish transparent liquid or waxy |
600~1000 |
1.08~1.2 |
20 |
|||
Materials preheat |
|||||||
A-2001: preheated at 50~60℃ for 8~10 hours. |
|||||||
B-8580: preheated at 50~60℃ for 8~12 hours. |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/74~76 |
7~9 |
50~60 |
0.13~0.16 |
45~55 |
4~5 |
The adding content of C-2 should be 300g±20g/18kg. |
|||||||
The adding content of water should be 0~90g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength(MPa) |
Elongation (%) |
Tear Strength |
/ |
|
Physical properties |
0.30~0.40 |
35~45 |
4.0~6.0 |
300~380 |
18~26 |
||
Demold time may be prolonged with the increase of sole thickness |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical establecido en 2007, el capital registrado de la compañía es de RMB 500 millones. Los productos principales son todos los rangos de poliéster poliol, resina de poliuretano para zapatos, resinas de poliuretano a base de agua y sin solventes para cuero artificial, adhesivos de unión de poliuretano y adhesivos de poliuretano en caliente.
Ahora Xuchuan tiene 4 bases de producción modernas, la capacidad de producción alcanzó 630,000 toneladas por año, productos exportados a 32 países y regiones en el mundo.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.